Advertising in MoldMaking Technology offers
Issue link: https://mmt.epubxp.com/i/617955
TIP 48 MoldMaking Technology —— JANUARY 2016 PVD Coatings and Tool Steel Selection MOLD MATERIALS By Mark Falkingham and Jereme Bohling Mold users are driving an increased use of physical vapor deposition (PVD) coatings, and this has generated questions and concerns from mold builders as they select materials from which to manufacture their molds. PVD coatings are a family of very thin (approximately 2 to 5 microns) metal layers applied in a vacuum chamber using a plasma process. To keep this in perspective, there are 25,400 microns in an inch or, in metric, a micron is equal to one mil- lionth of a meter. The PVD process is a line-of-sight process, which means that it can only coat what it can "see." When selecting the best option among the variety of avail- able PVD coatings, there are many factors to consider, most importantly wear resistance, lubricity and release. The primary advantage of these coatings is their ability to increase wear resistance over uncoated steel, as most PVD coatings are much harder than the steel substrate. This wear resistance is particu- larly beneficial for molding high-filled glass resins, which are especially abrasive. PVD coat- ings can also be used over an existing plating. Lubricity is the second main benefit of using PVD coatings on molds, as PVD eases the use of slide-type components and similar steels. The third main asset is release of the plastic part from the mold, as PVD helps to reduce part sticking and cycle time. And beyond just evaluating these three factors in general terms, a coating's micro-hardness (measured in Vickers) should be considered for wear, and its coefficient of friction for release and lubricity. Almost any PVD coating will be harder and "slipperier" than the steel onto which it is being applied. Once the moldmaker has identified the benefits it is look- ing to gain, it's time to examine the various considerations for selecting and using a PVD coating. For example, the PVD coat- ing is applied on top of the substrate, increasing component size by 1-4 microns. This is a factor the moldmaker must now take into consideration for the final build and function of the mold. Also, if the plastic component has fine detail, the vari- ance of the PVD coating to the steel component and how this could affect the final plastic part must be examined. When it comes to steel selection, the standard grades and heat-treat cycles might need to be changed depending on the selected PVD coating. The moldmaker must ensure that the application temperature of the PVD process is lower than the heat-treatment cycle temperature that is used on the steel. Lead time must be also considered, as the PVD process will be the last step prior to the mold build. This also makes it critical to catch any issues related to the steel selection and the PVD coating as early as possible. Lastly, if welding is required after the PVD process, there are certain steps that are required for removing the coating, and these steps vary by type of coating. To find the best solution, the customer must find the cor- rect coating for the application and then determine the proper steel to maximize the results. Too often customers allow the steel and heat treatment to determine the coatings that can be considered. The benefits of and considerations for PVD coat- ings should be discussed during the design of the mold build. Only then can the appropriate coating be applied in the cor- rect areas to improve product quality. CONTRIBUTOR Mark Falkingham is a process and applications engineer at eifeler Coatings Technology. Jereme Bohling is product manager for plastics applications at Bohler-Uddeholm Corporation. The PVD coating is applied on top of the substrate, increasing component size by 1-4 microns. This is a factor the moldmaker must now take into consideration for the fnal build and function of the mold. Image courtesy of Bohler-Uddeholm Corp. and eifeler Coatings Technology. PVD coatings are a family of very thin metal layers applied in a vacuum chamber using a plasma process. FOR MORE INFORMATION Bohler-Uddeholm Corporation / bucorp.com eifeler Coatings Technology / eifeler.us